Argedent Bio Yellow PF
High Gold Alloys for Ceramics
| Color | YELLOW |
| Type | 4 |
| ADA Class | HIGH NOBLE (HN) |
|
Application
  
|
|
| Processing | |
|---|---|
| Investment | Phosphate Bonded |
| Crucible | Graphite / Ceramic |
| Degassing Temp C | 650-1010 |
| Oxidation Procedure | Hold 3 Min, Do Not Remove Oxide, No Vacuum |
| Solder & Laser Wires | |
|---|---|
| PreSolder | YSF |
| PostSolder | 720 |
| Laser Wire | LWT86 |
| Physical Properties | |
|---|---|
| VHN After Firing | 220 |
| VHN Soft | |
| VHN Hard | 250 |
| Proof Stress Soft MPa | 550 |
| Proof Stress Hard MPa | 665 |
| Tensile Strength Soft MPa | 650 |
| Tensile Strength Hard MPa | 750 |
| Elongation Soft | 8 |
| Elongation Hard | 5 |
| Elastic Modulus GPa | 94 |
| Composition | |
|---|---|
| Gold (Au) | 86.5 |
| Indium (In) | 0.2 |
| Manganese (Mn) | 0.1 |
| Tantalum (Ta) | 0.3 |
| Zinc (Zn) | 1.5 |
| Iridium (Ir) | 0.1 |
| Platinum (Pt) | 10.4 |
| Rhodium (Rh) | 0.9 |
| Thermal Properties | |
|---|---|
| Melting Range C | 1040-1130 |
| Casting Temp C | 1280 |
| Density g/cc | 18.6 |
| Expansion at 500C | 14.3 |
| Expansion at 600C | 14.5 |
| Burnout Temp C | 800 |